Polyether Imide (PEI) Ultem 1010 is an amorphous, amber to transparent thermoplastics with a glass transition temperature (Tg) of 217 °C and performs in continuous use up to 170 °C. This inherently flame retardant plastic has UL94 V0 and 5VA ratings.
The PrimaCreator PEI Filament has unique properties because it does not come into contact with water during the production process and is directly packaged in a vacuum packaging. These properties make the PrimaCreator PEI Filament particularly suitable for usage in FDM and FFF 3D printers. The material has an excellent adhesion between layers which results in great improvement of the impact resistance, strength, durability and the printing process.
To make a successful PEI print there are a few things to keep in mind.
The printer must have the performance to meet the PEI filament and it should be printed with a nozzle temperature of 350-380°C. The heat bed should be set to 120-160°C and a heated chamber is important to have. It´s also very important to make sure that the printer is placed in a room where there´s hardly any draft and temperature fluctuations.
PEEK is best printed on a PEI sheet at a printing speed of 15-30 mm/s.
|Tolerance||± 0.05 mm|
|Heated build platform required||Yes, 120-160° C|
|Print Temperature||355 - 390° C|
|Recommended Print Speed||15-30 mm/s|
|Weight Filament||500 grams|
|Density||ISO 1183||1,27 g/cm3|
|Tensile Modulus||ISO 527||3200 MPa|
|Tensile Strength||ISO 527||105 MPa|
|Impact strength||ISO 180||5 KJ/m2|
|Filament Typ||PEI Ultem 1010|
|Recomended Printing Temp Min||355 ºC|
|Recomended Printing Temp Max||390 ºC|
|Recomended Printbed Temperature Min||120 ºC|
|Recomended Printbed Temperature Max||160 ºC|
|Recomended Printing Speed Min||20 mm/s|
|Recomended Printing Speed Max||35 mm/s|
|Specific gravity||1,27 g/cm3 ISO 1183|
|Mold Shrinkage||0,5 - 0,7%|
|Specific volume resistivity||1.0E+15 Ω*cm IEC 60093|
|Vicat softening temp||215 °C ISO 306/A50|
|Heat deflection temp||200 °C ISO 75-2/Be|
|Tensile strength||105 MPa ISO 527-2/50|
|Tensile modulus||3200 MPa ISO 572-2/1|
|Elongation at yield||6 % ISO 527-2/50|
|Elongation at break||60 % ISO 527-2/50|
|Flexural Strenght||160 % ISO 178|
|Flexural Modulus||3300 ISO 178|
|Impact Strength||5 KJ/m2 ISO 180-1A|